MIG Welding Wire; Filler Metal 5 to 6 Percent Silicon, 0.4 Percent Iron, 0.1 Percent Copper/Zinc, 0.05 Percent Manganese, 0.3 to 0.5 Percent Magnesium, 0.15 Percent Titanium, Less than 0.003 Percent Beryllium, Aluminum; Diameter 3/64 Inch; Melting Temperature 1065 to 1175 Deg F; Packaging Type Plastic Spool; Approval AWS/ASME SFA 5.10, CWB, ABS, VD TUV 1153; Voltage Rating 27 Volt; Current Rating 220 Amp; Type of Current Direct Current Electrode Positive GMAW, AC, GTAW; Wire Feed Speed Rating 390 IPM; Density 0.097 Pound per Cubic Inch; Anodized Color Gray; High Strength 35 KSI; Application Post Weld Age, Post Weld Heat Treat and Age, Automotive/Motorcycle Frame, Sports Product-Scooter/Bicycle, General Repair and Maintenance, Aerospace Hardware, Ladder and Frame, Alloy 356 Casting, Wheel, Ship Deck, Furniture

25% Higher UTS and 50% Higher Yield Strength than 4043 in the as Welded Condition (Typical); Moderate/High Strength (35 KSI Typical); Low Melting Temperature/High Fluidity; Low Welding Smut and Discoloration; Low Ductility, Formability and Lower Toughness (Similar to 4043); Moderate Electrical Conductivity and Thermal Conductivity; Post Weld Fully Heat Treatable Requiring No Base Metal Dilution; Excellent Corrosion Resistance; Low Shrinkage Rate/Reduced Distortion; Low Hot Cracking Sensitivity in Most Applications